Influence of partial dealumination of BEA zeolites on physicochemical and catalytic properties of AgAlSiBEA in H2-promoted SCR of NO with ethanol - Sorbonne Université Accéder directement au contenu
Article Dans Une Revue Microporous and Mesoporous Materials Année : 2016

Influence of partial dealumination of BEA zeolites on physicochemical and catalytic properties of AgAlSiBEA in H2-promoted SCR of NO with ethanol

Résumé

The two-step postsynthesis method allows obtaining AlSiBEA zeolites with different degree of dealumination (Si/Al = 100 and 200). Physicochemical properties (crystallinity, hydroxyl group coverage, acidic sites and nature of silver species) of AlSiBEA and AgAlSiBEA were investigated by XRD, DR UV–vis, XPS, TEM and FT-IR with CO and pyridine as probe molecules. Catalytic properties of the zeolites were studied in the process of selective reduction of NO with ethanol in the presence of hydrogen in the reaction mixture. It was shown that level of H2-promoting effect on the SCR-process depends on the dealumination degree of Ag-containing BEA zeolites and greater effect is observed for the catalysts with higher concentration of Lewis acidic sites.
Fichier principal
Vignette du fichier
Popovych_Influence_of.pdf (758.91 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01259919 , version 1 (21-01-2016)

Identifiants

Citer

Nataliia O. Popovych, Pavlo I. Kyriienko, Sergiy O. Soloviev, Svitlana M. Orlyk, Stanislaw Dzwigaj. Influence of partial dealumination of BEA zeolites on physicochemical and catalytic properties of AgAlSiBEA in H2-promoted SCR of NO with ethanol. Microporous and Mesoporous Materials, 2016, 226, pp.10-18. ⟨10.1016/j.micromeso.2015.12.031⟩. ⟨hal-01259919⟩
103 Consultations
151 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More