Mg–C System up to 20 GPa: Its Phase Diagram and Stable Magnesium Carbides

Vladimir Z Turkevich
  • Fonction : Auteur
Carlos Renero-Lecuna
Yixuan Zhao
  • Fonction : Auteur
Yann Le Godec
Timothy A Strobel
Wilson A Crichton
  • Fonction : Auteur
Nicolas Guignot
  • Fonction : Auteur
Hicham Moutaabbid
  • Fonction : Auteur
Ioannis Touloupas
  • Fonction : Auteur

Résumé

The phase diagram of the Mg−C system has been constructed up to 20 GPa and ∼4000 K based on complementary Thermo-Calc simulations and experimental data obtained in both ex situ and in situ experiments using X-ray diffraction with synchrotron radiation. Three high-pressure magnesium carbides, namely, β-Mg 2 C 3 , its high-temperature form γ-Mg 2 C 3 , and antifluorite Mg 2 C, have p−T domains of thermodynamic stability. At the same time, the carbides accessible by ambient-pressure synthesis, α-Mg 2 C 3 and MgC 2 , are either metastable or unstable, depending on the temperature, at least up to 20 GPa. Experimental observations show that at ambient conditions, all carbides are metastable and remain unchanged at least for years.
Fichier principal
Vignette du fichier
JPCC-2023-accepted.pdf (2.95 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04219981 , version 1 (27-09-2023)

Identifiants

Citer

Vladimir Z Turkevich, Carlos Renero-Lecuna, Yixuan Zhao, Yann Le Godec, Timothy A Strobel, et al.. Mg–C System up to 20 GPa: Its Phase Diagram and Stable Magnesium Carbides. Journal of Physical Chemistry C, 2023, 127 (4), pp.1965-1972. ⟨10.1021/acs.jpcc.2c07176⟩. ⟨hal-04219981⟩
8 Consultations
65 Téléchargements

Altmetric

Partager

More