Effect of vanadium dispersion and support properties on the catalytic activity of V-SBA-15 and V-MCF mesoporous materials prepared by direct synthesis - Sorbonne Université Accéder directement au contenu
Article Dans Une Revue Catalysis Today Année : 2011

Effect of vanadium dispersion and support properties on the catalytic activity of V-SBA-15 and V-MCF mesoporous materials prepared by direct synthesis

Résumé

Direct synthesis route was developed to support TiO2-ZrO2 binary metal oxide onto the carbon templated mesoporous silicalite-1 (CS-1). Metal hydroxide modified carbon particles could play a role as hard template and simultaneously support metal components on the mesopores during the crystallization of zeolites. Such supported TiO2-ZrO2 binary metal oxides (TZ/CS-1) showed better resistance to deactivation in the oxidative dehydrogenation of ethylbenzene (ODHEB) in the presence of CO2. These catalysts were found to be active, selective and catalytically stable (10 h of time-on-stream) at 600 °C for the dehydrogenation of ethylbenzene (EB) to styrene (Sty).
Fichier non déposé

Dates et versions

hal-00667426 , version 1 (07-02-2012)

Identifiants

Citer

Marco Piumetti, Barbara Bonelli, Pascale Massiani, Stanislaw Dzwigaj, Llenia Rossetti, et al.. Effect of vanadium dispersion and support properties on the catalytic activity of V-SBA-15 and V-MCF mesoporous materials prepared by direct synthesis. Catalysis Today, 2011, 176, pp.458-464. ⟨10.1016/j.cattod.2010.10.066⟩. ⟨hal-00667426⟩
94 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More