Large size crystalline vs. co-sintered ceramic Yb 3+ :YAG disk performance in diode pumped amplifiers - Sorbonne Université
Article Dans Une Revue Optics Express Année : 2015

Large size crystalline vs. co-sintered ceramic Yb 3+ :YAG disk performance in diode pumped amplifiers

Résumé

A comprehensive experimental benchmarking of Yb3+:YAG crystalline and co-sintered ceramic disks of similar thickness and doping level is presented in the context of high average power laser amplifier operation. Comparison is performed considering gain, depolarization and wave front deformation quantitative measurements and analysis.

Domaines

Optique [physics.optics]
Fichier principal
Vignette du fichier
oe-23-1-570.pdf (2.77 Mo) Télécharger le fichier
Origine Publication financée par une institution

Gestionnaire HAL 2 Sorbonne Université  : Connectez-vous pour contacter le contributeur

https://hal.sorbonne-universite.fr/hal-01277755

Soumis le : mardi 23 février 2016-10:30:43

Dernière modification le : jeudi 1 août 2024-13:48:05

Archivage à long terme le : dimanche 13 novembre 2016-01:39:13

Télécharger pour visualiser

Dates et versions

hal-01277755 , version 1 (23-02-2016)

Licence

Paternité

Identifiants

Citer

Daniel Albach, Jean-Christophe Chanteloup. Large size crystalline vs. co-sintered ceramic Yb 3+ :YAG disk performance in diode pumped amplifiers. Optics Express, 2015, 23 (1), pp.570-579. ⟨10.1364/OE.23.000570⟩. ⟨hal-01277755⟩

Exporter

BibTeX XML-TEI Dublin Core DC Terms EndNote DataCite

Collections

CEA X UPMC CNRS X-LULI X-DEP-PHYS DAM UNIV-PARIS-SACLAY SORBONNE-UNIVERSITE SU-SCIENCES GS-ENGINEERING IRAMIS
479 Consultations
348 Téléchargements

Altmetric

Partager

More