Bimodal Fucoidan-Coated Zinc Oxide/Iron Oxide-Based Nanoparticles for the Imaging of Atherothrombosis

Abstract : A polyol method was used to obtain ultrasmall ZnO nanoparticles (NPs) doped with iron ions and coated with a low molecular weight fucoidan in order to perform in vivo MR and ex vivo fluorescence imaging of athrothrombosis. During the synthesis, the early elimination of water by azeotropic distillation with toluene allowed us to produce NPs which size, determined by XRD and TEM, decreased from 7 nm to 4 nm with the increase of iron/zinc ratios from 0.05 to 0.50 respectively. For the highest iron content (NP-0.50) NPs were evidenced as a mixture of nanocrystals made of wurtzite and cubic phase with a molar ratio of 2.57:1, although it was not possible to distinguish one from the other by TEM. NP-0.50 were superparamagnetic and exhibited a large emission spectrum at 470 nm when excited at 370 nm. After surface functionalization of NP-0.50 with fucoidan (fuco-0.50), the hydrodynamic size in the physiological medium was 162.0 ± 0.4 nm, with a corresponding negative zeta potential of −48.7 ± 0.4 mV, respectively. The coating was evidenced by FT-IR spectra and thermogravimetric analysis. Aqueous suspensions of fuco-0.50 revealed high transverse proton relaxivities (T2) with an r2 value of 173.5 mM−1 s−1 (300 K, 7.0 T) and remained stable for more than 3 months in water or in phosphate buffer saline without evolution of the hydrodynamic size and size distribution. No cytotoxic effect was observed on human endothelial cells up to 48 h with these NPs at a dose of 0.1 mg/mL. After injection into a rat model of atherothrombosis, MR imaging allowed the localization of diseased areas and the subsequent fluorescence imaging of thrombus on tissue slices.
Document type :
Journal articles
Complete list of metadata

Cited literature [58 references]  Display  Hide  Download

https://hal.sorbonne-universite.fr/hal-02103819
Contributor : Hal Sorbonne Université Gestionnaire <>
Submitted on : Thursday, April 18, 2019 - 5:18:46 PM
Last modification on : Monday, December 14, 2020 - 9:43:54 AM

File

molecules-24-00962-v2.pdf
Publication funded by an institution

Identifiers

Citation

Hoang Nguyen, Eric Tinet, Thierry Chauveau, Frédéric Geinguenaud, Yoann Lalatonne, et al.. Bimodal Fucoidan-Coated Zinc Oxide/Iron Oxide-Based Nanoparticles for the Imaging of Atherothrombosis. Molecules, MDPI, 2019, 24 (5), pp.962. ⟨10.3390/molecules24050962⟩. ⟨hal-02103819⟩

Share

Metrics

Record views

474

Files downloads

1018