The corrosion behaviour of copper in aerated 0.1 M NaCl solution in presence of 8-aminoquinoline (8-AQ), using open circuit potential (OCP) measurements, potentiodynamic polarization, electrochemical impedance spectroscopy (EIS) measurements and atomic force microscopy (AFM), was studied. The measurements revealed that the effect of 8-AQ is dependent on its concentration. For concentrations up to 10−3 M, the organic compound displaces the corrosion potential following no trend and also reduces the anodic current. In contrast, for concentrations higher than 10−3, 8-AQ reduces markedly both, the anodic and cathodic currents and consequently, the corrosion current density of copper. After 9 days of exposure in chloride solution, containing the organic compound, potentiodynamic polarization analyses showed a significant reduction in the anodic response and a less significant reduction in the cathodic response, which is associated with a film formed at the copper surface of about 10 μm in thickness and visually observed by a colour change of the copper surface. In order to elucidate the most likely interaction between the 8-AQ molecule and the different molecular structures probably present on copper surfaces in chloride solutions, some results obtained from theoretical calculations are presented. The following molecular structures were considered: CuCl molecule, CuCl2− complex, and little copper clusters defect representation built as five atoms on C4v symmetry. Thus, based on the geometric, energetic, frontier orbital, and Total Electronic Density analysis done for the optimized states found for the systems investigated, we suggest that the most probable interaction of 8-AQ proceeds above CuCl units and free copper sites.