Chemistry of resistivity changes in TiTe/Al2O3 conductive-bridge memories
Résumé
We report the chemical phenomena involved in the reverse forming (negative bias on top electrode) and reset of a TaN/TiTe/Al2O3/Ta memory stack. Hard X-ray photoelectron spectroscopy was used to conduct a non-destructive investigation of the critical interfaces between the electrolyte (Al2O3) and the TiTe top and Ta bottom electrodes. During reverse forming, Te accumulates at the TiTe/Al2O3 interface, the TiOx layer between the electrolyte and the electrode is reduced and the TaOx at the interface with Al2O3 is oxidized. These interfacial redox processes are related to an oxygen drift toward the bottom electrode under applied bias, which may favour Te transport into the electrolyte. Thus, the forming processes is related to both Te release and also to the probable migration of oxygen vacancies inside the alumina layer. The opposite phenomena are observed during the reset. TiOx is oxidized near Al2O3 and TaOx is reduced at the Al2O3/Ta interface, following the O2− drift towards the top electrode under positive bias while Te is driven back into the TiTe electrode.
Domaines
Chimie
Origine : Publication financée par une institution
Loading...